  • Low Temperature Sintering and Dielectric Properties of (Ba,Ca)(Ti,Li)(O,F)3 Ceramics with High Permittivity
  • Published at:Not Found
  • Solid State Sciences 8 (2006) 922–926

      Laldja TAÏBI–BENZIADA, H. S. HILAL* and Régnault VON DER MÜHLL,


    Cold-pressed pellets were prepared from a powder mixture of BaTiO

    3 with 5 mol% of (CaF2 +LiF). The pellets were then air-fired at different temperatures (800, 930, 1000 or 1100 C) for different times (2, 4 or 8 h). Dielectric measurements were conducted at temperatures in the range 100–450 K with a wide frequency range, 100 Hz–40 MHz. Permittivity, εr , showed a diffuse ferroelectric–paraelectric phase transition at lower temperatures (263 K TC 368 K), where TC is the Curie temperature. In agreement with a non-relaxor ferroelectric behavior, the ferroelectric Curie temperature was frequency-independent. Dielectric dispersion was significant beyond 10 MHz. Ceramics sintered between 930 and 1100 C are promising candidates for future fabrication of class II capacitors.


    2006 Elsevier SAS. All rights reserved.

  • Bookmark and Share Email
Leave a Comment


  • No Attachments Found for this Article


Hikmat S. Hilal
Organometallics (organic and inorganic), Materials, Catalysis, Semiconductors, Photoelectro-chemistry
Show Full ProfileEnglish CV Arabic CV



Please do not email me if you do not know me
Please do not e-mail me if you do not know me