  • Modification of n-Si Characteristics by Annealing and Cooling at Different Rates
  • Published at:Active and Passive Electronic Components Volume 26 (2003), Issue 4, Pages 213-230doi:10.1080/0882751031000116124
  • The effect of annealing of the n-Si semiconductor on its characteristics in photoelectrochemical systems has been investigated. The annealing improved the dark current density vs. potential plots. The surface was improved by annealing, as manifested by SEM results. The effect of the cooling rate on preheated n-Si wafers was also investigated. It was found that the slowly cooled electrodes gave better dark current density vs. potential plots, for samples annealed at lower than 550°C. For samples annealed at higher temperatures, quenching gave better dark-current density vs. potential plots. SEM measurements showed parallel results to these findings. Enhanced surface textures were observed for slowly cooled wafers from temperatures below 550°C. Samples quenched from temperatures above 550°C showed better surfaces than slowly cooled counterparts.

     

     

     

    http://www.hindawi.com/GetArticle.aspx?doi=10.1080/0882751031000116124

     
  • Bookmark and Share Email
     
Leave a Comment

Attachments

  • No Attachments Found for this Article

PROFILE

Subhi Kamel Saleh
 
Show Full ProfileEnglish CV
 
 

PUBLISHED ARTICLES

 
Please do not email me if you do not know me
Please do not e-mail me if you do not know me